Inheritance of density, microfibril angle, and modulus of elasticity in juvenile wood of Pinus radiata at two locations in Australia

A total of 1640 increment cores from 343 radiata pine (Pinus radiata D. Don) families were sampled at two second-generation progeny trials, aged 6 and 7 years, for a detailed genetic study of juvenile wood quality traits. Density, microfibril angle (MFA), and modulus of elasticity (MOE) were determined from pith to bark using SilviScan (R) technology. Heritability was greatest for area-weighted density at the two sites (0.63 and 0.77, respectively), and the lowest for growth traits (<0.23). Genotype by environment interaction was low for all three wood quality traits. A positive genetic correlation between density and MOE (0.43), and a highly negative, and therefore, favourable genetic correlation between MFA and MOE (-0.92) were observed, implying that improvement of multiple juvenile wood properties is possible. The genetic correlations between whole-core wood quality traits and individual-ring measurements suggest that improvement for juvenile wood properties across the entire profile of the corewood including the innermost rings can be achieved. However, density, MFA, and MOE had unfavourable genetic correlations with diameter growth suggesting that selection for increased density and MOE, and reduced MFA in the absence of selection for growth will result in a genetic loss for growth rate.